	title = {High Temperature Structural Study of Gd-Doped Ceria by Synchrotron X-ray Diffraction (673 K <= T <= 1073 K)},
	journal = {Inorganic Chemistry},
	volume = {53},
	note = {{\textquoteright}doi: 10.1021/acsenergylett.0c01132\n - I.Am.Hydrogen{\textquoteright}
{\textquoteright}\n - jyoungstrom{\textquoteright}
{\textquoteright}Jason thinks this is great.\n~\n - jyoungstrom{\textquoteright}
{\textquoteright}\n - estechel{\textquoteright}
},
	pages = {10140-10149},
	abstract = {The crystallographic features of Gd-doped ceria were investigated at the operating temperature of solid oxides fuel cells, where these materials are used as solid electrolytes. (Ce1{\textendash}xGdx)O2-x/2 samples (x = 0.1, 0.3, 0.5, 0.7) were prepared by coprecipitation of mixed oxalates, treated at 1473 K in air, and analyzed by synchrotron X-ray diffraction in the temperature range 673 K <= T <= 1073 K at the Elettra synchrotron radiation facility located in Trieste, Italy. In the whole temperature span a boundary was found at x \~{} 0.2 between a CeO2-based solid solution (for x <= 0.2) and a structure where Gd2O3 microdomains grow within the CeO2 matrix, taking advantage of the similarity between Gd3+ and Ce4+ sizes; the existence of the boundary at x \~{} 0.2 was confirmed also by measurements of ionic conductivity performed by impedance spectroscopy. Similar to what observed at room temperature, the trend of the cell parameter shows the presence of a maximum; with increasing temperature, the composition corresponding to the maximum moves toward lower Gd content. This evidence can be explained by analyzing the behavior of the coefficient of thermal expansion as a function of composition.},
	issn = {0020-1669},
	doi = {10.1021/ic5011242},
	url = {https://doi.org/10.1021/ic5011242},
	author = {Cristina Artini and Marcella Pani and Andrea Lausi and Roberto Masini and Giorgio A. Costa}
}